A systematic study of the structural and magnetic properties of the RM
o1.5Fe10.5Nx series, where R is Y, Ce, Pr, Nd, Sm, Gd, Th, Dy, Ho, or
Er, has been carried out using x-ray diffraction, magnetic measurement
s, and the Mossbauer effect. The 1-12 phase with Ce and Pr has been su
ccessfully stabilized. PrMo1.5Fe10.5Nx possesses excellent intrinsic m
agnetic proper-ties, favorable for permanent magnet applications. The
1-12 phase, RMo1.5Fe10.5Nx, was also stabilized. Compared to RMo2Fe10N
x, this compound shows a higher Curie temperature and a larger saturat
ion magnetization due to the lower Mo content.