A. Inoue et al., New bulk amorphous Fe-(Co,Ni)-M-B (M=Zr,Hf,Nb,Ta,Mo,W) alloys with good soft magnetic properties, J APPL PHYS, 83(11), 1998, pp. 6326-6328
We have found that an amorphous phase with a wide supercooled liquid region
reaching 85 K before crystallization is formed in Fe-(Co, Ni)-(Zr, Nb, Ta)
-B, Fe-Co-(Zr, Nb)-(Mo, W)-B and Co-Fe-Zr-B systems. The high stability of
the supercooled liquid enabled the production of bulk amorphous alloys with
diameters up to 5 mm by copper mold casting. These amorphous Fe-(Co, Ni)-M
-B alloys exhibit good soft magnetic properties, i.e., saturation magnetiza
tion of 0.95 to 1.1 T, low coercivity of 1 to 8 A/m, Curie temperature of 5
60 to 590 K and low magnetostriction of 8 - 14 x 10(-6). The effective perm
eability of the Co-based alloys exceeds 25 000 at 1 kHz and keeps high valu
es above 5000 at the high frequency of 1 MHz. The permeability at 1 MHz is
much higher than those for any kinds of soft magnetic materials. The freque
ncy at which the imaginary part of permeability shows a maximum is also abo
ut 1 MHz. The success of synthesis of new Fe- and Co-based amorphous alloys
with good soft magnetic properties and high glass-forming ability is promi
sing for future development of a new type of soft magnetic material. (C) 19
98 American Institute of Physics. [S0021-8979(98)47111-1].