Novel lactamimide-containing polymers were first synthesized by the bisimid
e-lacramimide ring contraction of 1,8:4,5-tetracarboxylic bisimide-containi
ng polymers. The conversion of bisimide moieties was in the range 68-100% d
epending on polymer chain flexibility. The yields of lactamimide units were
between 75 and 100% with respect to bisimide group conversion owing to the
insolubility of polymers during lactam ring closure. No appreciable hydrol
ytic degradation of polymers was observed as followed from GPC data. Both u
.v. long-wave absorption and emission maxims in polylactamimides were 20-50
nm red shifted compared with those of polyimides due to intramolecular cha
rge transfer. It was found that the thermostability of lactamimide units wa
s close to that of bisimide as proved by TGA. (C) 1999 Elsevier Science Ltd
. All rights reserved.