Alumina-supported gallium oxide catalysts for NO selective reduction: Influence of the local structure of surface gallium oxide species on the catalytic activity
K. Shimizu et al., Alumina-supported gallium oxide catalysts for NO selective reduction: Influence of the local structure of surface gallium oxide species on the catalytic activity, J PHYS CH B, 103(9), 1999, pp. 1542-1549
The surface structure of alumina-supported gallium oxide catalysts for sele
ctive catalytic reduction of NO by CH4 was studied. The XPS results showed
that Ga atoms were dispersed well over the Al2O3 surface for the samples wi
th Ga2O3 content below monolayer coverage (27 wt %) and that Ga2O3 particle
s appeared at higher content. The XANES and EXAFS results revealed that, be
low monolayer coverage, Ga atoms were located at the surface cation sites (
tetrahedral and octahedral) of Al2O3, and the fraction of tetrahedral Ga sp
ecies decreased as Ga content increased. The activity per surface area of t
he catalysts increased with Ga2O3 content up to around the monolayer covera
ge and declined at higher content. Below monolayer coverage, the activity p
er exposed Ga atom decreased as Ga content increased, which correlated well
with the change in the fraction of tetrahedral Ga species. It was conclude
d that the present reaction is a structure-sensitive reaction depending on
the local structure of Ga atom; GaO4 tetrahedra highly dispersed in the sur
face spinel are responsible for the activity.