Cm. Giordano et al., THE EFFECT OF CU2-CORROSION CRACKING SUSCEPTIBILITY OF ALPHA-BRASS INCUPRIC NITRATE SOLUTIONS( CONCENTRATION ON THE STRESS), Corrosion science, 39(10-11), 1997, pp. 1915-1923
The stress corrosion cracking (SCC) susceptibility of alpha-brass in a
queous cupric nitrate solutions was studied. The effect of the Cu2+ io
n concentration on the stress corrosion crack propagation rate (CPR) w
as measured. A linear relationship between the logarithm of the CPR an
d the logarithm of the Cu2+ concentration was found in all the alloys
studied. The slope of this relationship was very close to that reporte
d for the cuprous ion exchange current density and the cupric ion conc
entration: delta log i(o(Cu+-->Cu))/delta log [Cu2+]. All the cracks f
ound were transgranular, and the crack propagation mechanism was expla
ined through the surface mobility SCC mechanism. (C) 1997 Elsevier Sci
ence Ltd.