EFFECT OF POLARIZATION ON CRACK INITIATION AND DISLOCATION BEHAVIOR NEAR-THE-SURFACE OF A537 STEEL DURING LOW-CYCLE CORROSION-FATIGUE IN 3.5-PERCENT NACL SOLUTION
Jq. Wang et al., EFFECT OF POLARIZATION ON CRACK INITIATION AND DISLOCATION BEHAVIOR NEAR-THE-SURFACE OF A537 STEEL DURING LOW-CYCLE CORROSION-FATIGUE IN 3.5-PERCENT NACL SOLUTION, Journal of materials science letters, 17(4), 1998, pp. 345-348