Ds. Schmidt et al., LITHIATED NICKEL-OXIDE ELECTRODE PERFORMANCE IN MOLTEN K2S2O7 V2O5 AND K2SO4/V2O5 SYSTEMS/, Journal of the Electrochemical Society, 145(3), 1998, pp. 892-897
Citations number
24
Categorie Soggetti
Electrochemistry,"Materials Science, Coatings & Films
Lithiated nickel oxide (LixNiyO) electrodes have been successfully use
d with molten K2S2O7/V2O5 at 400 degrees C and K2SO4/V2O5 at 480 and 5
20 degrees C in the electrochemical membrane removal of sulfur oxides
from simulated flue gases,The porous gas-diffusion electrodes manufact
ured in the laboratory from commercial Ni electrode material remained
stable and conductive in this environment for periods up to 40 days. P
olarizations are reported in these systems for current densities up to
50 mA/cm(2). The results show exchange current densities from 0.113 m
A/cm(2) at 400 degrees C to 0.8 mA/cm(2) at 520 degrees C.