Y. Niu et al., THE SULFIDATION OF A CU-15 VOL.PERCENT NB ALLOY IN H-2-H2S MIXTURES AT 400-600-DEGREES-C, Oxidation of metals, 49(1-2), 1998, pp. 169-186
The corrosion of a Cu-15 vol.% Nb alloy by H-2-H2S mixtures has been s
tudied under 10(-12) atm S-2 at 400 and 500 degrees C and under 10(-10
) atm S-2 at 500 and 600 degrees C. The alloy is a two-phase mixture o
f the two terminal solid solutions and is composed of a Cu-rich matrix
containing particles of the Nb-rich phase elongated parallel to the s
ample surface and isolated mainly from each other. The alloy corroded
at rates similar to those of pure copper at 400 and 500 degrees C unde
r 10(-12) atm S-2, but more slowly than pure copper at 500 and 600 deg
rees C under 10(-10) atm S-2. The scales were duplex, containing an ex
ternal layer of pure copper sulfide and an inner very porous region co
mposed of a mixture of sulfides of the two metals in which, however, t
he core of the large Nb particles was still uncorroded.