Jx. Yang et al., STUDY ON THE LITHIUM SOLID ELECTROLYTES OF LI3N-LI3BI-LICL TERNARY-SYSTEM - 2LI(3)BI-CENTER-DOT-3LICL LITHIUM SOLID-ELECTROLYTE, Solid state ionics, 96(3-4), 1997, pp. 215-218
Lithium solid electrolyte 2Li(3)Bi . SLiCl was prepared and was charac
terized by X-ray diffraction and X-ray photoelectron spectroscopy (XPS
). The electrical conductivity of the prepared sample was determined f
rom room temperature to 250 degrees C by PAR 368-1 AC-impedance spectr
ometer. The frequency measurement range was between 4 Hz and 100 kHz.
The experimental results showed that the 2Li(3)Bi . 3LiCl lithium soli
d electrolyte has a high conductivity of about 1 x 10(-4) S/cm at 100
degrees C and 1 x 10(-2) S/cm at 350 degrees C.