M. Tabuchi et al., Results of a Japanese round robin on creep crack growth evaluation methodsfor Ni-base superalloys, ENG FRACT M, 62(1), 1999, pp. 47-60
Creep crack growth (CCG) tests on Ni-base superalloys were carried out in t
he Japanese VAMAS group as part of a round-robin program in order to assist
the standardization of the CCG test method for creep-brittle alloys. The e
ffect of temperature, load, specimen thickness and material microstructure
on CCG behavior was investigated. The applicable range of fracture mechanic
al parameters to evaluate the CCG rate was evaluated. The CCG rate was char
acterized by the C* parameter independent of testing conditions in the rang
e where the CCG rate accelerated. However, the acceleration stage occupied
only a small portion of life time for the creep-brittle superalloys. In the
range where the CCG rate was constant, the CCG rate and the fracture life
could be predicted approximately by the Q* method based on the thermally ac
tivated process. (C) 1998 Elsevier Science Ltd. All rights reserved.