The non-isothermal devitrification of a lithium titanium germanate glass of
stoichiometry Li2TiGe3O9 has been studied by differential thermal analysis
. The temperature of maximum nucleation rate and the value of activation en
ergy for crystal growth were evaluated from DTA curves. The influence on th
e crystallization process of the specific surface area of the samples and o
f the heat treatments of nucleation is emphasized. The investigated glass e
xhibited the same molar ratio of GeO6/GeO4 groups and the same T-g as lithi
um tetragermanate glass. (C) 1998 Elsevier Science B.V.