Welding of Alloy 718 is known to cause intergranular cracks in the wel
d heat-affected zone (HAZ). In this work, an Alloy 718 sample that exh
ibited HAZ cracking revealed high Cu/Zn concentrations on the fracture
surface. Previous studies on HAZ cracking of Alloy 718 have not repor
ted high Cu/Zn concentrations on the fracture surface. It is proposed
here that the presence of liquid Cu/Zn can cause liquid-metal embrittl
ement (LME) and HAZ cracking in Alloy 718.