MAGNETOOPTICAL ROTATION OF HEAVY-METAL OXIDE GLASSES

Citation
Cb. Pedroso et al., MAGNETOOPTICAL ROTATION OF HEAVY-METAL OXIDE GLASSES, Journal of non-crystalline solids, 231(1-2), 1998, pp. 134-142
Citations number
32
Categorie Soggetti
Material Science, Ceramics
ISSN journal
00223093
Volume
231
Issue
1-2
Year of publication
1998
Pages
134 - 142
Database
ISI
SICI code
0022-3093(1998)231:1-2<134:MROHOG>2.0.ZU;2-B
Abstract
Magneto-optical rotation was measured at room temperature for glasses containing Bi2O3-CdO-GeO2 (BCG); and Bi2O3-PbO-GeO2-B2O3 (BPGP), A pul sed magnetic field between 50 and 80 KG was used to measure Faraday ro tation at 632.8 nm as a function of the concentration of Bi and Cd for BCG and Bi and Pb for BPGB. Verdet constant as high as 0.162 min G(-1 ) cm(-1) at 632.8 nm for the BPGB sample with the highest concentratio ns of Bi and Cd was found. Verdet constant Increases linearly with the heavy-metal concentration for the BPGB whereas it reaches some satura tion for the BCG system. Measurements of the magneto-optical rotation at other wavelengths in the visible and the refractive index at 632,8 nm are also reported. (C) 1998 Elsevier Science B.V. All rights reserv ed.