To investigate the effect. of Al2O3 on the reduction and high temperat
ure properties of sintered ores, the heating-up reduction of sintered
ores varying the Al2O3 content are carried out. The early softening, t
he increase of pressure drop, and meltdown temperature were observed a
t lower temperature with increase of Al2O3 content. From the simultane
ous X ray observation of reduction process and EPMA and SEM analysis o
f quenched samples, a relatively large amount of Wustite-Gehlenite eut
ectic phase was observed in the early stage of reduction process at hi
gh Al2O3 content sintered ores. Based on these results, it is conclude
d that Al2O3 rich molten phase was produced at the relatively low temp
erature with the increase of Al2O3 content.