Fe nanowire arrays have been grown on self-organized NaCl(110) grating
s. The typical wire size is 42 nm x13 nm x10 mu m, with a period of ap
proximately 90 nm, The magnetic properties were dominated by a strong
in-plane shape anisotropy, Coherent switching dominated the reversal p
rocess due to dipole coupling ascribed to narrow gaps between the wire
s, The small width and height of the individual wires prevented domain
wall formation. Electron holography has been used to confirm the type
of ferromagnetic coupling between the wires. Experimental results are
compared with quantitative three-dimensional micromagnetics calculati
ons.