Hy. Woo et al., SYNTHESIS AND OPTICAL-PROPERTIES OF POLYURETHANES CONTAINING A HIGHLYNLO ACTIVE CHROMOPHORE, Macromolecular chemistry and physics, 199(7), 1998, pp. 1427-1433
Two types of new polyurethanes with a highly NLO active chromophore, 2
-[4-[4-[bis(2-hydroxyethyl)amino] phenylazo] benzylidene] malonitrile
(HAPM), in the polymer side chain were synthesized (PU1-DCN and PU2-DC
N) and characterized. The diisocyanate components of the polymers are
2,4-tolylene diisocyanate and 3,3'-dimethoxybiphenyl-4,4'-ylene diisoc
yanate. The molecular weights of PU1-DCN and PU2-DCN were determined t
o be <(M)over bar (w)> = 23000 (<(M)over bar (w)>/<(M)over bar (n)> =
2.19) and <(M)over bar (w)> = 22000 (<(M)over bar (w)>/<(M)over bar (n
)> = 2.34), respectively. The final products are readily soluble in po
lar aprotic organic solvents, like tetrahydrofuran, N,N-dimethylformam
ide, cyclohexanone, etc. Good optical quality films were obtained by s
pin coating. The glass transition temperatures of both polymers were f
ound to be 158-159 degrees C. They showed no melting points in the DSC
curves, suggesting an amorphous phase. It was found that the electro-
optic coefficient of PU1-DCN was r(33) = 62.7 pm.V-1 at 633 nm wavelen
gth. The macroscopic second-order hyperpolarizability at 1064 nm wavel
ength was determined to be chi((2)) = 136 pm.V-1 for PU1-DCN and chi((
2)) = 120 pm.V-1 for PU2-DCN.