D. Peramunage et Km. Abraham, THE LI5TI5O12 /PAN ELECTROLYTE//LIMN2O4 RECHARGEABLE BATTERY WITH PASSIVATION-FREE ELECTRODES/, Journal of the Electrochemical Society, 145(8), 1998, pp. 2615-2622
Citations number
20
Categorie Soggetti
Electrochemistry,"Materials Science, Coatings & Films
The Li-ion cell, Li4Ti5O12//PAN electrolyte//LiMn2O4, appears to be a
classic example of a battery with passivation-free electrodes. Its gro
ss impedance characteristics remain steady during long-term cycling at
high charge/discharge rates. The cell showed excellent rechargeabilit
y at >99.9% coulombic efficiency for nearly 250 full-depth cycles, at
a 1C discharge rate and a C/5 charge rate. The capacity fade was low a
t approximately 0.12% per cycle at around 100 cycles and similar to 0.
05% at around 200 cycles. Excellent utilizations of the cathode and an
ode were observed with values of 100 mAh/g of LiMn2O4 and 140 mAh/g of
Li4Ti5O12 at 1C discharge rate, and 70 mAh/g of LiMn2O4 and 92 mAh/g
of Li4Ti5O12 at 7.5C discharge rate. Electrode utilizations were signi
ficantly better under pulse discharge conditions at the 8C-16C rates.
The energy density of the cell, calculated with a cell voltage of 2.6
V and practically observed cathode and anode capacities at the C/10 di
scharge rate, is 60 Wh/kg. The weights of the electrodes, current coll
ectors, and electrolyte are included in this value. It is suitable for
applications where high power and very long cycle life are required.