S. Nakayama et M. Sakamoto, ELECTRICAL-PROPERTIES OF NEW-TYPE HIGH OXIDE IONIC CONDUCTOR RE10SI6O27 (RE = LA, PR, ND, SM, GD, DY), Journal of the European Ceramic Society, 18(10), 1998, pp. 1413-1418
Electrical properties of the high oxide ionic conductive ceramic RE10S
i6O27 (RE = La, Pr, Nd, Sm, Gd, Dy) sintered at 1700-1800 degrees C by
the use of MgO-stabilized zirconia setter during a sintering have bee
n investigated The lowest activation energy and the highest conductivi
ty at 200 degrees C were achieved for Pr10Si6O27 (55.4 kJ mol(-1)) and
La10Si6O27 (1.32x10(-5) S cm(-1)), respectively. The conductivity of
La10Si6O27 at 200 degrees C was higher by order of 1.5x10(1) times tha
n that (8.82x10(-7) S cm(-1) at 200 degrees C) of (Bi2O3)(0.75)(Y2O3)(
0.25). The three-point bending strength of La10Si6O27 was 100 MPa. (C)
1998 Elsevier Science Limited. All rights reserved.