PROTONIC AND NATIVE CONDUCTION IN SR-SUBSTITUTED LAPO4 STUDIED BY THERMOELECTRIC-POWER MEASUREMENTS

Measurements of the thermoelectric power were applied to investigate t he electrical conductivity in 5 mol % Sr-substituted LaPO4 as a functi on of temperature (600 to 900 degrees C), water vapor partial pressure (0.2 to 6 kPa), and oxygen partial pressure (4 to 100 kPa). Expressio ns of the thermoelectric power for materials conducting protons, oxide ions, and electronic defects were derived, based on a thermodynamic t reatment of entropy production by heat and charge transfer. The experi mental data for 5 mol % Sr-substituted LaPO4 were interpreted in terms of protonic conduction, and some additional conduction, possibly by e lectron holes. In air, the proton transport number is unity at 600 deg rees C when p(H2O) > 1 kPa, and at 700 degrees C when P-H2O > 3 kPa. I n wet atmospheres, the transported entropy of protons in this material was found to be nearly constant, 112 +/- 2 J mol(-1) K-1 at 600 to 80 0 degrees C in wet atmospheres.