The Gibbs energy of formation of the solution and compound phases in t
he Nb-Sn system were derived from an optimization procedure using all
the available experimental thermodynamic and phase diagram data. The t
hermodynamic description of the intermetallic compounds was made using
a sublattice model, while a Redlich-Kister polynomial was used for th
e solution phases.