Lf. Chua et Hw. Kui, CORRELATION FOR THE GLASS-FORMING ABILITY OF PD83.5-XCUXSI16.5 WITH CRYSTALLINE-COMPOUND SOLID-SOLUTION FORMATION/, Journal of applied physics, 84(11), 1998, pp. 5993-5996
Molten Pd83.5-xCuxSi16.5 alloys, where 0 less than or equal to x less
than or equal to 27, were allowed to crystallize at temperatures not t
oo far removed from their liquidus T-1. The crystalline phases in the
as-crystallized specimens were then identified. An attempt was made to
correlate the glass forming ability of Pd83.5-xCuxSi16.5 alloys with
the crystalline phases formed upon their solidification from the molte
n state. (C) 1998 American Institute of Physics. [S0021-8979(98)02323-
8]