Gv. Kurlyandskaya et al., Magnetoimpedance effect in CoFeNi plated wire with ac field annealing destabilized domain structure, J APPL PHYS, 85(8), 1999, pp. 5438-5440
Giant magnetoimpedance (GMI) behavior at 0.25 MHz has been studied for a co
mposite wire consisting of a 1 mu m thick Co6Fe20Ni74 magnetic layer electr
oplated onto a 0.1 mm diam CuBe nonmagnetic wire. This has been done for as
-deposited samples as well as after annealing under dc and ac axial magneti
c fields. In the optimum conditions, a maximum GMI of 150% is achieved. The
observed GMI hysteresis in the as-prepared state decreases for high drivin
g current used to measure the MI itself. Such hysteresis, to be avoided in
technological applications, is also very much reduced after ac field anneal
ing. GMI characteristics are analyzed considering the domain-wall stabiliza
tion occurring after the annealing treatments. (C) 1999 American Institute
of Physics. [S0021-8979(99)17208-6].