Structural analysis and magnetic properties of the 1-D compounds [M(NCS)(2)bpa(2)] [M = Fe, Co, Ni and bpa = 1,2-bis(4-pyridyl)ethane]

The increasing interest in designing polymeric compounds has focused this w ork on the synthesis and magnetostructural characterization of three 1-D co mpounds of general formula [M(NCS)(2)bpa(2)] [M = Fe, Co, Ni and bpa = 1,2- bis(4-pyridyl)ethane] which exhibit double bpa bridges between metallic cat ions. X-Ray single crystal diffraction analysis was carried out on 1 [Fe(NC S)(2)bpa(2)] while for 2 [Co(NCS)(2)bpa(2)] and 3 [Ni(NCS)(2)bpa(2)] the st ructural characterization was performed on powdered samples. UV-VIS results were consistent with high-spin metallic cations in tetragonally distorted octahedral fields. Although in the three compounds weak antiferromagnetic c oupling has been observed taking place through the -M-(bpa)(2)-M- bridges, for the theoretical analysis of the global magnetic behaviour of all of the m some other effects have been considered, i.e. zero field splitting and sp in-orbit coupling.