C. Tranquilan-aranilla et al., Kappa-carrageenan-polyethylene oxide hydrogel blends prepared by gamma irradiation, RADIAT PH C, 55(2), 1999, pp. 127-131
A composite hydrogel system from kappa-carrageenan (KC) and polyethylene ox
ide was prepared by gamma irradiation, KC was blended with low (LPEO) and m
edium (MPEO) molecular weight PEO having a concentration of 5% (w/w) at a r
atio of 1:1. The properties of the blended hydrogels were evaluated in term
s of gel fraction, swelling behavior and gel strength. KC/MPEO hydrogel sys
tem has a gel content of 75% at a dose of 10 kGy while 60% gel content was
noted for KC/LPEO at the same dose. Water gain of more 10,000% was exhibite
d by both systems investigated. Gel strength of KC/MPEO was higher compared
to KC/LPEO hydrogel. KC/MPEO hydrogel retained 88% (364 N) of its gel stre
ngth even after autoclave sterilization. (C) 1999 Elsevier Science Ltd. All
rights reserved.