Low temperature preparation and fuel cell properties of rare earth doped barium cerate solid electrolytes

The solid electrolytes, BaCe(0.8)Ln(0.2)O(2.9) (Ln: Gd, Sm, Eu), were prepa red by the sol-gel method. XRD indicated that a pure orthorhombic phase was formed at 900 degrees C. The synthesis temperature by the sol-gel method w as about 600 degrees C: lower than the high temperature solid phase reactio n method. The electrical conductivity and impedance spectra were measured a nd the conduction mechanism was studied. The grain-boundary resistance of t he solid electrolyte could be reduced or eliminated by the sol-gel method. The conductivity of BaCe0.8Gd0.2O2.9 is 7.87 x 10(-2) S.cm(-1) at 800 degre es C. The open-circuit voltage of hydrogen-oxygen fuel cell using BaCe0.8Gd 0.2O2.9 as electrolyte was near to 1 V and its maximum power density was 30 mW.cm(-2).