Photoinduced alignment of polymer liquid crystals containing azobenzene moieties in the side chain. 5. Effect of the azo contents on alignment behavior and enhanced response
Yl. Wu et al., Photoinduced alignment of polymer liquid crystals containing azobenzene moieties in the side chain. 5. Effect of the azo contents on alignment behavior and enhanced response, MACROMOLEC, 32(12), 1999, pp. 3951-3956
A series of side-chain polymer liquid crystals (PLCs) of 6-[4-(4-ethylpheny
l)diazenylphenyloxy]hexyl methacrylate and 4'-[6-(methacryloyloxy)hexyloxy]
-4-cyanobiphenyl were synthesized and characterized. The effects of content
s of the azo units and the wavelength of irradiation light on photoinduced
alignment behavior were investigated. On irradiation of linearly polarized
light (LPL) at 366 nm directly, alignment change was induced only in the PL
C with 6 mol % azo units (P6), while phase transition took place in the oth
er PLCs with higher contents of the azo units. On irradiation of LPL at 436
nm directly, alignment was induced with a fair efficiency in P15 and P35,
low efficient alignment was observed in P6 and P100, and no alignment chang
e was induced in P55 and P75, which exhibited a homeotropic state. A high a
lignment efficiency was achieved in all PLCs by using another method: irrad
iation with 366 nm unpolarized light at first and then with 436 nm LPL. The
alignment change induced by this method was explored at various temperatur
es. All-optic switching might be realized by irradiation of 336 nm unpolari
zed light and 436 nm LPL alternatively based on the photochemical phase tra
nsition and the photoinduced alignment processes of the PLCs, respectively.