Effect of attritor milling on the densification of magnesium aluminate spinel

Citation
R. Sarkar et al., Effect of attritor milling on the densification of magnesium aluminate spinel, CERAM INT, 25(5), 1999, pp. 485-489
Citations number
11
Categorie Soggetti
Apllied Physucs/Condensed Matter/Materiales Science","Material Science & Engineering
Journal title
CERAMICS INTERNATIONAL
ISSN journal
02728842 → ACNP
Volume
25
Issue
5
Year of publication
1999
Pages
485 - 489
Database
ISI
SICI code
0272-8842(1999)25:5<485:EOAMOT>2.0.ZU;2-L
Abstract
Densification of magnesium aluminate spinel was studied with both the singl e stage and double stage sintering processes using attritor mill for the re duction of particle size. Presynthesized spinel and a stoichiometric mixtur e of calcined magnesia and alumina were used for the study. Presynthesizati on of spinel and calcination of raw materials were done at 1400 and 1600 de grees C. Milling was done for 2, 4 and 6 h. Extent of milling was character ised by measuring the specific surface area of the milled powders. Densific ation was found to be greatly influenced by milling. A maximum 99.5% densif ication was obtained. (C) 1999 Elsevier Science Limited and Techna S.r.l. A ll rights reserved.