Ef. El-wahidy et al., Effect of iron content and annealing temperature on the corrosion behaviorof Ni100-xFex, J MATER SCI, 34(12), 1999, pp. 2971-2978
Ni100-xFex metallic glasses have been prepared with 8.5 less than or equal
to x less than or equal to 51 using electrodeposition technique. Corrosion
behavior of specimens in 0.1 M Na2SO4 (pH = 6) at 25 degrees C has been stu
died using potential-time decay, linear polarization resistance and potenti
odynamic techniques. Anodic polarization curves show that the specimens exh
ibit quasi-passive region. The dissolution of samples increases with the in
crease of iron concentration and also with the increase of annealing temper
ature. The interpretation was based on the enhanced dissolution of the form
ed microcrystals of the specimens in the sulphate solution. (C) 1999 Kluwer
Academic Publishers.