Composite structures, using MWNT and SWNT and the polymer PmPV exhibit prop
erties which enhance those of the individual components. The polymer PmPV c
an act as an organic filter for the multiwalled system where the MWNT are i
ndefinitely suspended in the polymer solution while the carbonaceous materi
al falls out of solution. Raman measurements of this show a complete reduct
ion of the amorphous line at 1350 cm-1. We see that we can alter the lumine
scence quantum yield of the composite, where the effects are different depe
nding on which nanotubes are used. When we examine the SWNT/PmPV the quantu
m yield is increased. The MWNT composite also shows strong non-linear optic
al signal. The pristine polymer has an chi((3)) of 10(-11) esu whereas the
composite chi((3)) is -10(-10) esu.