XAFS spectra near K absorption edges of Pt (78.4 keV) and Pb (88.0 keV) wer
e measured in transmission mode with Si (511) planes of an adjustable incli
ned double-crystal monochromator at bending-magnet beamline BL01B1 at SPrin
g-8. The energy resolution was estimated as good as 7 eV at Pt K-edge, bene
fitted from the high brilliant x-rays from the SPring-8 storage ring. Blunt
edge jumps and reduction of MAPS amplitude were observed owing to the fini
te lifetime of the core hole as predicted theoretically. Local structure pa
rameters have been successfully evaluated from EXAFS signal above the Kedge
.