Dielectric and thermal expansion properties of LHPG grown potassium lithium niobate single crystals

Compositions of potassium lithium niobate K6Li4+xNb10O30 (x for excess mole % of Li2O) with tetragonal tungsten bronze structure were prepared as cryst al fibers by the Laser Heated Pedestal Growth technique. The lattice consta nts of KLN were measured by using X-ray diffraction and typical values for a = 12.5703 +/- 0.0018 and c = 3.9485 +/- 0.0012 were measured. This paper reports the dielectric permittivity measurements on single crystal along th e a- and c- axis in the temperature range of 90-450K and frequency range of 10(2)-10(5) Hz. The dielectric permittivity at room temperature along a- a nd c- axis was 430 and 330 respectively. Mechanism for the low temperature dielectric relaxation will be discussed. Thermal expansion behavior in the a- and the c-direction will also be reported.