Coexistence of ferroelectricity and ferromagnetism in BiFeO3-BaTiO3 thin films at room temperature

(Bi0.7Ba0.3) (Fe0.7Ti0.3)O-3 films have been constructed on Nb-doped SrTiO3 (100) by the pulsed-laser deposition technique, and their physical propert ies have been examined. The films exhibit both ferroelectricity and ferroma gnetism (weak ferromagnetism) with P-r=2.5 mu C/cm(2) and M-r=0.2 emu/g at room temperature. The film-thickness dependence of their magnetic and elect ric properties (size effect) is also discussed simultaneously. The dielectr ic constants of the films decrease with reducing film thickness below 1000 Angstrom. The magnetic Curie temperature of the films, on the other hand, d oes not change at all down to 250 Angstrom. (C) 1999 American Institute of Physics. [S0003-6951(99)02130-0].