D. Kaczorowski et al., Magnetic, thermodynamic, and electrical transport properties of ternary equiatomic ytterbium compounds YbTM (T=transition metal, M=Sn and Bi), PHYS REV B, 60(1), 1999, pp. 422-433
Physical behavior of several YbTM intermetallics has been studied by means
of x-ray powder diffraction, magnetization, dc magnetic susceptibility, hea
t capacity, and electrical resistivity measurements. The compounds YbTBi wi
th T = Cu, Ag, An and YbTSn with T = Ag, Au, Zn were shown to be nonmagneti
c due to the presence of divalent ytterbium ions. The bismuthide YbPdBi as
well as the stannides YbRhSn and YbPtSn were found to exhibit localized mag
netism of almost trivalent Yb ions. The electrical behavior of these three
phases is characteristic of dense Kondo systems, and their low-temperature
specific heat data indicate a possible heavy fermion ground state. [S0163-1
829(99)12525-6].