H. Nishizawa et al., Formation of alpha,beta-type hydroxides and second-stage intermediate in hydrothermal decomposition of nickel acetate, J SOL ST CH, 146(1), 1999, pp. 39-46
During heating of nickel acetate solution at a constant rate of 4 degrees C
/min up to 350 degrees C, alpha-type anion-exchangeable layered hydroxide N
i-2(OH)(3)(OCOCH3)1.4H(2)O, containing the acetate anions in the interlayer
spaces, first crystallized at 160 degrees C. A second-stage intermediate p
hase losing the acetate guest in every second layer appeared at 180 degrees
C and subsequently transformed at 210 degrees C to slightly disordered bet
a-Ni(OH)(2) phase with a small amount of acetate anions. beta-Ni(OH)(2) pha
ses were gradually losing the acetate guest with increasing temperature, an
d perfectly ordered hexagonal-shaped beta-Ni(OH)(2) crystals with a mean di
ameter of 10 mu m were obtained at 320 degrees C. Above 340 degrees C, dehy
dration of beta-Ni(OH)(2) to NiO occurred. (C) 1999 Academic Press.