Id. Olekseyuk et al., PHASE-EQUILIBRIA OF AG33.3SN16.7SE50-CDSE SECTION OF THE QUASI-TERNARY AG2SE-CDSE-SNSE2 SYSTEM, Polish Journal of Chemistry, 71(6), 1997, pp. 721-724
The interaction between components of polythermal Ag33.3Sn16.7Se50-CdS
e section of quasiternary Ag2Se-CdSe-SnSe2 system was investigated and
its T-x projection was established using differential thermal, X-ray
phase, microstructural analysis and microhardness measurements. The Ag
2CdSnSe4 compound was found melting incongruently at 908 K and exhibit
ing orthorhombic structure (space group Cmc2(1)) with lattice constant
s a = 0.4263(3), b = 0.7372(2), c = 0.6811(2) nm.