H. Takahashi et al., Perpendicular uniaxial magnetic anisotropy of Fe16N2(001) single crystal films grown by molecular beam epitaxy., IEEE MAGNET, 35(5), 1999, pp. 2982-2984
The uniaxial magnetic anisotropies by torque measurement have been measured
for Fe16N2(001) single crystal films grown by molecular beam epitaxy (MBE)
. It has been found that Fe16N2(001) films exhibits perpendicular uniaxial
anisotropy which makes the easy axis along the [001] direction, and those a
nisotropy constants K-U1 and K-U1 for Fe16N2 were 1.6 X 10(7) and 0.4 X 10(
7) erg/cm(3), respectively. Those K-U1 and K-U2 for Fe16N2 were constant in
the thickness range from 34 to 83nm, The ferromagnetic resonance of Fe16N2
(001) single crystal films have been measured. The saturation magnetic flux
densities, 4 pi M-S for Fe16N2 measured by the magnetic torques and resona
nce fields agreed well with the values measured with a vibrating sample mag
netometer (VSM).