Thinning procedures were observed by TEM in 310 stainless steel and pure al
uminum. Foils thinned through shearing of mode III crack or through tearing
of mode I crack. Using micro-beam electron diffraction, the strains in the
areas right ahead of crack tips of pure aluminum and TiAl alloy were measu
red to be 0.05 or more.