Hs. Chauhan et M. Murakami, Enhancement of J(c) by refinement of Nd4Ba2Cu2O10 particles in OCMG processed Nd-Ba-Cu-O system with Pt and CeO2 addition, MAT SCI E B, 65(1), 1999, pp. 48-53
We have melt-grown the Nd-Ba-Cu-O superconductor from the precursor with a
composition of NdBa2Cu3Oy + 10% Nd4Ba2Cu2O10 + 0.5 wt% Pt + 1.0 wt% CeO2 in
0.1% O-2-Ar environment. A combined addition of Pt and CeO2 has resulted i
n the refinement of Nd4Ba2Cu2O10 (Nd422) particles down to submicron size a
s revealed by optical and transmission electron microscopic observations. A
large enhancement of critical current density reaching 10(5) A cm(-2) in a
self field at 77 K has been accomplished as a result of fine dispersion of
Nd422. (C) 1999 Elsevier Science S.A. All rights reserved.