A. Hernando et al., Magnetic behaviour during the first crystallisation stages in Co-B amorphous alloys: A test of the exchange penetration through interfaces, NANOSTR MAT, 11(6), 1999, pp. 783-788
Two amorphous compositions of the Co-B system, which present quite differen
t magnetic behaviour, have been studied in the as-cast state and after low
temperature annealings. The Co80B20 amorphous alloy submitted to thermal tr
eatments undergoes a primary crystallisation which transforms the material
into a two phase system composed of nanocrystals of cobalt embedded in a Co
-B amorphous matrix. The role of the cobalt grains on the magnetisation pro
cesses and the coercive field is analysed for temperature ranging from 77 t
o 300 K. It is found that the hardening effect of the grains diminishes on
increasing the temperature. The large crystalline anisotropy of the Co grai
ns as well as the magnetic state of the grain boundary which transmits the
exchange interaction, are mainly responsible for the observed behaviour. (C
)1999 Acta Metallurgica Inc.