Thermoelectric properties of ceramic samples of NiO doped with Li are studi
ed in the temperature range of 450-1280 K, with different Li contents. The
substitution of Li for Ni atoms in a cubic NiO lattice results in a high th
ermoelectric power factor over a wide temperature range. Furthermore: Li su
bstitution decreased the thermal conductivity resulting in an increase in t
he thermoelectric figure of merit, Z = 0.75 x 10(-4) K-1 over 1000 K, sugge
sting that NiO is a promising oxide-base material for high-temperature ther
moelectric devices.