Results of a detailed X-ray diffraction and thermal analysis study of the s
tructural phase transitions in LiKSO4 carried out in the temperature range
123-1000 K are presented. The study indicates five phase transitions in the
temperature range studied at 937, 707, 226 (268), 200 (251), and 186 (190)
K (values in parentheses are for a warming process). The transition at 226
(268) K is reported for the first time. The different phases (from high to
low temperature) show the space groups P6(3)/mmc, P2(1)cn, P6(3), P6(3)mc,
P3(1)c, and Cmc2(1). The working conditions allowed us to obtain the differ
ent phases without twin crystals and without mixtures of several phases. We
were thus able to determine the crystal structures of the different phases
with more accuracy. The transitions at high temperature produce large vari
ations in the crystal structure and the enthalpy of process is high, while
at low temperature, as the structure is more compact, an activation energy
is necessary, and the transitions show a thermal hysteresis, while the stru
ctural variation is as small as the enthalpy of the process. (C) 1999 Acade
mic Press.