Transformation behaviour in thermomechanically processed C-Mn-Si TRIP steels with and without Nb

Two 0.2wt.% C-1.55wt.% Mn-1.5wt.% Si steels with and without the addition o f 0.039 wt.% Nb were studied by laboratory simulations of controlled thermo mechanical processing in a quench deformation dilatometer. The microstructu res were characterised using optical metallography, image analysis and scan ning electron microscopy techniques. The effects of recrystallised and non- recrystallised austenite and discontinuous paths on the final microstructur e were studied. The results have shown that the highest volume fraction of retained austenite is associated with a 400 degrees C isothermal bainite tr ansformation temperature and the presence of approximately 50% polygonal fe rrite and acicular ferrite as a dominant second phase. (C) 1999 Elsevier Sc ience S.A. All rights reserved.