Structure characteristics and valence state study for La1-xNaxTiO3 synthesized under high-pressure and high-temperature conditions

By using a novel high-pressure, high-temperature method, perovskite oxides of La1-xNaxTiO3 (x = 0.05, 0.1-0.8) with mixed valence state were synthesiz ed. XRD analysis shows a cubic cell for the samples. Cell volumes of the sa mples with 0.1 less than or equal to x less than or equal to 0.5 decreases as x increases, and the cell Volume for x = 0.05 is smaller than that for x = 0.1. XPS of surface and EPR measurements indicate that Ti ions are of mi xed valence of +3 and +4 and that A-cations vacancies exist in the samples. As x increases, the amount of Ti3+ ions decreases and the amount of A-cati ons vacancies increases. The valence state of Ti ions can be altered by cha nging both pressure and temperature. (C) 2000 Elsevier Science B.V. All rig hts reserved.