Pseudoelasticity (PE) is clearly seen in Fe-28Mn-6Si-5Cr shape memory alloy
exhibiting non-thermoelastic martensitic transformation, especially in the
sheets hot rolled with a low finishing temperature (FT). Comparison betwee
n the temperature dependence of PE and that of shape memory effect (SME) in
dicates that the gamma double left right arrow epsilon transformation is re
sponsible not only for the SME but also for the PE. As a result of consider
ation including variations in 0.2% proof stress and 2.0% flow stress with t
emperature, it is concluded that PE depends on the amount of the deformatio
n due to the gamma --> epsilon transformation, the external stress and some
temperature-dependent effects which balance against the 'back stress' on u
nloading. Effects of temperature and low-FT hot rolling on PE are discussed
on the bases of the above-mentioned factors. Published by Elsevier Science
S.A.