The melt-spun ribbons of Nd8Fe85Mo1B6 have been prepared by directly rapid
quenching at different wheel speeds. From the result of vibrating sample ma
gnetometer measurement, we found that the magnetic properties of the ribbon
s are dependent on the wheel speed. X-ray diffraction and thermomagnetic an
alysis were also used to investigate microstructure and phase composition o
f the samples. The result shows that the TbCu7 phase increases with increas
ing wheel speed; at the same time, a decreased grain size of the alpha-Fe p
hase is observed. The change of magnetic properties is due to the change of
phase composition arid grain size of the samples.