Cellulose-based polycaprolactone (CAPCL) sheets were prepared from cellulos
e acetate (CA) and epsilon-caprolactone (CL). Thermal properties of the obt
ained CAPCL's were studied by differential scanning calorimetry (DSC), ther
mogravimetry (TG) and TG-Fourier transform infrared spectrometry (TG-FTIR).
The glass transition temperatures (T-g 's) of CAPCL decreased with increas
ing CL / OH ratio, until CL/OH ratio reached 15 and then increased above th
at ratio. Melting of CAPCL was observed when CL/OH ratio was over 10. The t
hermal degradation temperatures (T-d 's) of CAPCL increased from ca. 350 de
grees C to 390 degrees C with increasing CL/OH ratio. The results obtained
by TG-FTIR analysis of CAPCL showed that gases with OH, CH, C=O, C-O-C grou
ps evolved by thermal degradation.