Y. Kang et al., Synthesis and conductivity of PEGME branched poly(ethylene-alt-maleimide) based solid polymer electrolyte, B KOR CHEM, 21(2), 2000, pp. 241-244
A thermally stable comb-like polymer electrolyte, poly(ethylene glycol) mon
omethyl ether (PEGME) grafted poly(ethylene-alt-maleimide), has been synthe
sized and characterized. The copolymer was thermally stable up to 250 degre
es C and had good film forming property. The copolymer was well mixed with
poly(ethylene glycol) dimethyl ether(PEGDME, (M) over bar w = 400). The act
ivation energy of ionic conduction decreased and conductivity increased wit
h the increase of PEGDME content in the polymer electrolyte. The maximum co
nductivity of the resulting polymer electrolyte containing 66 wt% of PEGDME
was found to be 3 x 10(-4) S/cm at 30 degrees C. The polymer electrolyte s
howed electrochemical stability window of greater than 4.7 V.