Xb. Fan et T. Ishigaki, Mo5Si3-boron composites fabricated by induction plasma deposition and their high-temperature oxidation resistance, J AM CERAM, 82(8), 1999, pp. 1965-1968
Induction plasma spraying was used to produce freestanding parts of Mo5Si3-
boron (Mo5Si3-B) composite materials. Four different Mo5Si3-B compositions
were prepared and oxidized isothermally at 1210 degrees C in air at atmosph
eric pressure. The high-temperature oxidation performance of these material
s was dependent strongly on the boron content in the specimens. The composi
te that contained 2.0 wt% boron exhibited excellent resistance to oxidation
, as indicated by the almost-zero change in specimen mass after oxidation f
or 24 h.