The anatase phase of titania has been stabilized without chemically mo
difying the system, by changing the level of packing within the aggreg
ates by freeze-drying the water-washed precipitate obtained by the hyd
rolysis of titanium isopropoxide. After calcination at 700 degrees C f
or 8 h, freeze-dried samples showed more than 97% anatase phase with a
surface area and porosity of 29 m(2) g(-1) and 37% respectively. The
oven-dried samples showed a surface area and porosity of 5 m(2) g(-1)
and 10% respectively.