Magnetization and electrical resistivity measurements have been carried out
on ternary intermetallic compounds of the formula RRhAl (R = La, Ce, Pr, N
d and Gd). These compounds with R = La and Ce crystallize in the orthorhomb
ic Pd-2(MnPd)Ge-2 type structure while those with R = Pr, Nd and Gd crystal
lize in the orthorhombic TiNiSi type structure, all in the space group Pnma
. The compound LaRhAl exhibits superconductivity below 2.4 K while PrRhAl,
NdRhAl and GdRhAl are ferromagnetically ordered with Curie temperatures of
about 5, 10 and 30 K, respectively. The compound CeRhAl shows mixed valent
behaviour of the Ce ions and is neither magnetically ordered nor supercondu
cting down to 1.7 K. (C) 2000 Elsevier Science Ltd. All rights reserved.